| 摘要 |
<p>In a double-sided adhesive tape in which acrylic-based adhesive layers are formed on respective sides of an electron beam cross-linked polyethylene foam substrate, the acrylic-based adhesive layers are formed from a cured resin composition formed by irradiating a solvent-free photopolymerizable monomer composition containing an acrylic-based monomer and a photopolymerization initiator with ultraviolet rays to photo-polymerize the acrylic-based monomer. The cured resin composition contains an adhesion-imparting polymer having a weight average molecular weight of 2,000 to 10,000, an acrylic-based polymer A obtained by photopolymerization in the absence of a cross-linking agent and having a weight average molecular weight of 700,000 to 3,000,000, and an acrylic-based polymer B obtained by photopolymerization in the absence of a cross-linking agent and having a weight average molecular weight of 350,000 to 650,000. The molecular weight distribution of the cured resin composition measured by gel permeation chromatography using tetrahydrofuran is 2.4 to 4.4.</p> |