Cold worked, machined, and carburized quenched case-hardened steel prevented from formation of coarse grains, that is, case-hardened steel superior in cold workability, machinability, and fatigue characteristics after carburized quenching characterized by limiting, by mass%, S: 0.001 to 0.15%, Ti: 0.05 to 0.2%, Al: 0.04% or less, and N: 0.0050% or less, containing other specific ingredients in specific ranges, furthermore containing one or more of Mg: 0.003% or less, Zr: 0.01% or less, and Ca: 0.005% or less, limiting the amount of precipitation of AlN to 0.01% or less, and having a density d (/mm 2 ) of sulfides with a equivalent circle diameter of over 20 µm and an aspect ratio of over 3 and a content of S [S] (mass%) satisfying d‰¤1700[S]+20. |