摘要 |
An electric and electronic part copper alloy sheet with excellent bending workability and stress relaxation resistance is made from a copper alloy containing 1.5 to 4.0 percent by mass of Ni, Si satisfying a Ni/Si mass ratio of 4.0 to 5.0, 0.01 to 1.3 percent by mass of Sn, and the remainder composed of copper and incidental impurities, wherein the average crystal grain size is 5 to 20 mum, the standard deviation of the crystal grain size satisfies 2sigma<10 mum, and the proportion of the number of particles having a particle diameter of 90 to 300 nm in Ni-Si dispersed particles having a particle diameter of 30 to 300 nm is 20% or more, where the particles are observed in a cross-section defined by a direction perpendicular to a sheet surface and a direction parallel to a rolling direction.
|