<p>A high-strength galvanized steel sheet having excellent formability that has a TS of 780 MPa or more and is excellent in terms of ductility, stretch flangeability, and bendability; and a method for manufacturing the high-strength galvanized steel sheet are provided. The high-strength galvanized steel sheet having excellent formability has a component composition containing, on the basis of mass percent, 0.05 to 0.2% C, 0.5 to 2.5% Si, 1.5 to 3.0% Mn, 0.001 to 0.05% P, 0.0001 to 0.01% S, 0.001 to 0.1% Al, and 0.0005 to 0.01% N, the balance being Fe and incidental impurities; and the steel sheet has a microstructure including a ferritic phase and a martensitic phase including a tempered-martensitic phase, the ferritic phase having an area fraction of 30% or more relative to an entirety of the microstructure, the martensitic phase having an area fraction of 30 to 50% relative to the entirety of the microstructure, and the tempered-martensitic phase having an area fraction of 70% or more relative to an entirety of the martensitic phase.</p> |