| 摘要 |
The use of an ammonium hydroxide spike to a hot tetra methyl ammonium hydroxide (TMAH) solution to form an insitu poly oxide decapping step in a polysilicon (poly) etch process, results in a single step rapid poly etch process having uniform etch initiation and a high etch selectivity, that may be used in manufacturing a variety of electronic devices such as integrated circuits (ICs) and micro electro-mechanical (MEM) devices. The etching solution is formed by adding 35% ammonium hydroxide solution to a hot 12.5% TMAH solution at about 70° C. at a rate of 1% by volume, every hour. Such an etch solution and method provides a simple, inexpensive, single step self initiating poly etch that has etch stop ratios of over 200 to 1 over underlying insulator layers and TiN layers. |