| 摘要 |
<p><P>PROBLEM TO BE SOLVED: To provide a method of brazing plated products, a method that is free from generation of deposits due to flux burning and that is excellent in permeability of filler metal and formation of fillet in brazed joint. <P>SOLUTION: In a method of brazing plated products, after flux is applied to brazing parts 2a, 2b of joining members, the brazing parts 2a, 2b are heated and brazed under an inert gas atmosphere and then, plating is performed as post processing, wherein the flux is diluted to be 10-40 wt.% in effective component concentration. Also, the brazing temperature of the brazing parts 2a, 2b is set in a range not lower than liquidus temperature of the filler metal 9 and not higher than active temperature upper limit value of the flux. <P>COPYRIGHT: (C)2011,JPO&INPIT</p> |