| 摘要 |
It is an object of the present invention to provide a coated steel sheet, properties of which such as tape peeling resistance, solvent resistance, alkali resistance and abrasion resistance are improved. A coated steel sheet coated with a composite coat, wherein said composite coat comprises a compounded resin (A) in which polyurethane resin particles (A-1) and ethylene-unsaturated carboxylic acid copolymerization resin particles (A-2), respectively having an average particle diameter of 20 to 100 nm and a silanol group and/or an alkoxysilyl, group, are contained in a mass ratio of 20:80 to 90:10 and silicon oxide particles (A-3) having an average particle diameter of 5 to 20 nm and an organic titanium compound (A-4) are compounded, polyolefin wax particles (B) having an average particle diameter of 0.5 to 4 μm and a softening point of 100 to 140° C., and silicon oxide particles (C) having an average particle diameter of 70 to 200 nm, and wherein an amount of a coat of said composite coat is 0.5 to 3 g/cm2.
|