| 摘要 |
An epoxy resin represented by general formula (I), which satisfies numerical formula (1) mentioned below and comprises hydrolytic halogen of 0.05 wt. % or less, said epoxy resin being produced by the procedure as follows: after dissolving 0.8 to 1.3 mole of epihalohydrin to 1 mole of divalent phenol in a solvent, a pre-reaction is performed over 30 to 70 minutes by adding dropwise 0.25-0.35 mole of 30˜50% aqueous solution of alkali metal hydroxide over 30 to 70 minutes thereto, and thereafter, 0.65-0.75 mole of the remaining 30˜50% aqueous solution of alkali metal hydroxide is added dropwise over about 1 hour to complete the reaction over 1 to 3 hours. wherein n is an integer of 0 or more; A1 and A2 are residue of divalent phenol, and can be same or different; both R1 and R2 are H or wherein, X: epoxy equivalent (g/eq); Y: phenolic hydroxyl group equivalent (g/eq).
|