| 摘要 |
A high-strength hot-dip galvanized steel sheet that even on the premise of ordinary CGL heat cycle, has a low yield stress and excels in resistance to natural aging and baking hardenability without reliance on the use of expensive Mo; and a process for producing the same. The constituent composition thereof comprises 0.01 to less than 0.08% C, 0.2% or less Si, more than 1.0 to 1.8% Mn, 0.10% or less P, 0.03% or less S, 0.1% or less Al, 0.008% or less N and more than 0.5% Cr so that the relationship 1.9<=Mn(mass%)+1.3Cr(mass%)<=2.8 is satisfied and comprising the balance iron and unavoidable impurities. The structure thereof has a ferrite phase and a martensite phase of 2 to 15% area ratio, and the cumulative area ratio of pearlite phase and/or bainite phase is 1.0% or less. In the production of this hot-dip galvanized steel sheet, the temperature and cooling rate are controlled during the annealing/plating operation subsequent to cold rolling. |