VERFAHREN ZUR HERSTELLUNG EINER ELEKTRODE FÜR NICHTWÄSSRIGE ELEKTROLYTISCHE ZELLEN

摘要

A method for industrial and simplified production of an electrode for a non-aqueous electrolyte battery without unfavorable peeling of the electrode coating layer while maintaining the flexibility of the electrode is provided. An electrode for a non-aqueous electrolyte battery is produced by mixing an electrode active material with a polymer material substantially having no melting point at not higher than 300 DEG C to prepare an electrode coating-material, applying the electrode coating-material onto an electrode collector, drying the electrode having the coating layer formed, and then carrying out a heating treatment at a temperature not higher than 300 DEG C for less than 30 hours before or after compression-molding. The heating temperature is preferably 100 to 300 DEG C, and the heating time is preferably 30 minutes to 24 hours.