MOLDED ARTICLE AND METHOD FOR PRODUCING THE SAME

摘要

Disclosed is a molded article composed of a fiber-reinforced composite material (I) containing a continuous reinforcing fiber and a thermosetting matrix resin, and a thermoplastic resin member (II) which is joined to and integrated with at least a part of the surface of the fiber-reinforced composite material (I) by using a thermoplastic resin (A). The joined surface between the thermoplastic resin (A) and the fiber-reinforced composite material (I) has projections and recesses in the cross-section in the thickness direction of the molded article, and the maximum impregnation depth h of the thermoplastic resin (A) in the fiber-reinforced composite material (I) is not less than 10 µm. The thermoplastic resin (A) has a tensile strength at break of not less than 25 MPa and a tensile elongation at break of not less than 200%. The impact adhesive strength at the joined portion of the fiber-reinforced composite material (I) and the thermoplastic resin member (II) is not less than 3,000 J/m².