The aluminum alloy is an aluminum-magnesium-scandium-zirconium alloy having a long term corrosion resistance combined with high strength as compared to standard AA 5052 alloy, and is suitable for use in marine and salt water environments with a minimum of corrosion. The aluminum alloy contains about 2.2-3.0 wt. % magnesium, about 0.1-0.97 wt. % scandium, and about 0.14-0.9 wt. % zirconium. The alloy may also contain about 0.1-0.4% wt. % iron, 0.001-0.2 wt. % chromium, 0.02-0.94 wt. % titanium, and silicon, copper, zinc and manganese up to about 0.20 wt. %, 0.1 wt. %, 0.1 wt. %, and 0.01 wt. %, respectively, either as additives intentionally added during processing or as impurities, the remainder being aluminum.
|