| 摘要 |
A laminated film obtained by carrying out anti-reflection processing on the surface of a reflection polarizing film. This laminated film comprising (A) a monoaxially oriented laminated film consisting of 501 or more alternating first layers made of a first thermoplastic resin having a positive stress optical coefficient and a thickness of 0.05 to 0.5 mum and second layers made of a second thermoplastic resin different from the first thermoplastic resin and having a thickness of 0.05 to 0.5 mum, and a low-reflectance layer formed on at least one side of the monoaxially oriented laminated film and having a reflectance of the surface measured from the input side of 3% or less. This laminated film is characterized in that the average reflectance of a polarization component parallel to the plane including the stretching direction of the monoaxially oriented laminated film and a direction perpendicular to the film plane is 90% or more at a wavelength of 400 to 800 nm, and the average reflectance of a polarization component perpendicular to the plane including the stretching direction and the direction perpendicular to the film plane is 10% or less at a wavelength of 400 to 800 nm, and is used in a reflection type polarizing plate.
|