A glass composition is disclosed. The glass composition includes base glass composition including SiO<SUB>2 </SUB>from 65 to 75 weight percent, Na<SUB>2</SUB>O from 10 to 20 weight percent, CaO from 5 to 15 weight percent, MgO from 0 to 5 weight percent, Al<SUB>2</SUB>O<SUB>3 </SUB>from 0 to 5 weight percent, K<SUB>2</SUB>O from 0 to 5 weight percent, and BaO from 0 to 1 weight percent, and a colorant and property modifying portion including total iron from up to 0.02 weight percent, CeO<SUB>2 </SUB>from 0.05 weight percent to 1.5 weight percent, CoO up to 50 PPM, Se up to 15 PPM, Cr<SUB>2</SUB>O<SUB>3 </SUB>up to 500 PPM, CuO up to 0.5 weight percent, V<SUB>2</SUB>O<SUB>5 </SUB>up to 0.3 weight percent, TiO<SUB>2 </SUB>up to 1 weight percent, NiO up to 200 PPM, Er<SUB>2</SUB>O<SUB>3 </SUB>up to 3 weight percent, MnO<SUB>2 </SUB>up to 0.6 weight percent, and Nd<SUB>2</SUB>O<SUB>3 </SUB>up to 2 weight percent, wherein the glass composition has a redox ratio up to 0.55.
|