摘要 |
The invention relates to steel for hot tooling, the composition of said steel being made up of the following weight percentages: 0.30 % = C = 0.39 %, 4.00 % = Cr = 6.00 %, traces = Si = 0.50 %, traces = Mn = 0.80 %, traces = W = 1.45 %, traces = Co = 2.75 %, 0,80 % = Ni = 2.80 %, 1.50 % = Mo = 2.60 % with 1.50 % = Mo + 0.65W = 3.20 %, 0.55 % = V = 0.80 %, with 0.65 = K = 0.65, where K = K2 - K1 and K2 = 0.75 x (Ni 0.60), K1 = 1.43 x (V 0.40) + 0.63 x [(Mo + 0.65W) 1.20], traces = Al = 0.080 %, traces = S = 0.0040 %, traces = P = 0.0200 %, traces = Ti = 0.05 %, traces = Zr = 0.05 %, traces = Nb = 0.08 %, traces = N = 0.040 %, 10 P + As + 5 Sb + 4 Sn = 0.21 %, traces = O = 30ppm, the remainder being iron and inevitable impurities. The invention also relates to a part produced from said steel, to the method for the production thereof, and to the use of the same. |
申请人 |
AUBERT & DUVAL;BINOT, NICOLAS;GRELLIER, ANDRE;RICHY, PIERRE-EMMANUEL |
发明人 |
BINOT, NICOLAS;GRELLIER, ANDRE;RICHY, PIERRE-EMMANUEL |