摘要 |
<p>The present invention relates to a flaky a-alumina crystal and a preparation method thereof. More particularly, the present invention relates to a flaky a- alumina crystal comprising aluminum oxide and zinc oxide, which is prepared by hydrolyzing an aluminum precursor solution containing a water-soluble flux and a zinc precursor solution to obtain a gel mixture and aging, drying, calcining and crystallizing it under a specific reaction condition, and a preparation method thereof. Since the flaky a-alumina crystal of the present invention has a thickness of less than 0.5 µm, an average particle diameter of at least 15 µm and an aspect ratio of at least 50, it is useful as high-quality pearlescent pigment material and filler for ceramic materials.</p> |
申请人 |
KOREA RESEARCH INSTITUTE OF CHEMICAL TECHNOLOGY;CQV CO., LTD.;LEE, JUNG-MIN;PARK, BYUNG-KI;SUH, JEONG KWON;CHANG, KIL WAN;LIM, KWANG SU;JO, SUNG YUN;KANG, KWANG, CHOONG |
发明人 |
LEE, JUNG-MIN;PARK, BYUNG-KI;SUH, JEONG KWON;CHANG, KIL WAN;LIM, KWANG SU;JO, SUNG YUN;KANG, KWANG, CHOONG |