| 摘要 |
<p>A polypropylene-based resin composition for injection foam molding, containing (A) 50 to 95 parts by weight of a linear polypropylene-based resin having a melt flow rate of from 10 g/10 min. to 100 g/10 min. and a melt tension of 2 cN or less and (B) 5 to 50 parts by weight of a modified polypropylene having a melt flow rate of from 0.1 g/10 min. to less than 10 g/10 min. and a melt tension of 5 cN or more and exhibiting a strain hardening property (provided that a total of the resin (A) and the resin (B) is 100 parts by weight) and a foaming agent are supplied to an injection molding machine to be injected into a die, thereby achieving a foammolding. It is thus possible to obtain a injection foamed molded article which has a satisfactory injection foam moldability, a skin layer having little silver streaks or the like on its surface, and an internal core layer having a foam of high expansion ratio and uniformly fine and a excellent appearance glossiness, lightweightness, and rigidity at a low cost.</p> |