| 摘要 |
In order to provide a fluoro-rubber composite which hardly reduces a clean degree of a manufacturing environment and in which any of cracks is hardly generated, a rubber material using the same, and a method of manufacturing a fluoro-rubber molded product, a fluoro rubber is mixed with a tetrafluoroethylene/propylene system copolymer or a tetrafluoroethylene/propylene/vinylidenefluoride system copolymer, and a fluorine thermoplastic resin, and the resulting mixture is compounded with a peroxide cross-linking agent, and a co-cross-linking agent, and if necessary, any other suitable filler or the like, thereby obtaining a fluoro-rubber composite, and cross-linking is performed for the resulting fluoro-rubber composite, thereby obtaining a fluoro-rubber molded product. A cross-linking method, for example, is such that a predetermined amount of fluoro-rubber composite is filled in a mold having a desired shape, and primary cross-linking is performed for the fluoro-rubber composite through a heat process, and if necessary, secondary cross-linking may be performed for the fluoro-rubber composite in an oven at 150 to 250° C. for 1 to 32 hours. The fluoro-rubber molded product can have an arbitrary shape such as a sheet-like shape, a rod-like shape, a ring-like shape, or any of various complicated block-like shapes in correspondence to its application.
|