HOT PRESSING METHOD FOR HIGH STRENGTH MEMBER USING STEEL SHEET AND HOT PRESSED PARTS |
摘要 |
The present invention provides a method of hot pressing using hot rolled and cold rolled steel sheet or Al-based plated steel sheet or Zn-based plated steel sheet enabling a strength of at least 1200 MPa to be obtained after high temperature forming and with extremely little possibility of hydrogen embrittlement and such hot pressed parts, that is, a method of hot pressing a high strength automobile parts comprising using steel sheet containing as steel compositions by wt% C:0.05 to 0.5% or steel sheet plated mainly with Al or Zn to produce automobile members by hot pressing during which making the heating temperature before pressing Ac 3 or more to 1100°C or less, making the hydrogen concentration in the heating atmosphere 6 vol% or less, and making the dew point 10°C or less and such hot pressed parts. |
申请公布号 |
CA2573226(A1) |
申请公布日期 |
2006.01.19 |
申请号 |
CA20052573226 |
申请日期 |
2005.07.15 |
申请人 |
NIPPON STEEL CORPORATION |
发明人 |
MAKI, JUN;KUSUMI, KAZUHISA;OHGAMI, MASAHIRO;ABE, MASAYUKI;NAKAJIMA, SHINYA;FUJITA, NORIHIRO |
分类号 |
B21D22/20;B21D53/88;C23C2/06;C23C2/12;C23C2/40 |
主分类号 |
B21D22/20 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|