摘要 |
A polymer pipe for hot fluids, usually hot water is described. The pipe is characterised in that it comprises a multimodal polyethylene with a high molecular weight (HMW) fraction and a low molecular weight (LMW) fraction where said HMW fraction has a density of at least 0.920 g/cm<SUP>3</SUP>, and that the multimodal polyethylene has a density of 0.921-0.950 g/cm<SUP>3 </SUP>and has a time to failure at 95° C. and 3.6 MPa of at least 165 h determined according to DIN 16 833 and a modulus of elasticity of at most 900 MPa determined according to ISO 527-2/1B. Preferably, the multimodal polyethylene is a bimodal polyethylene, the LMW fraction having a density of 0.955-0.975 g/cm<SUP>3</SUP>, the HMW fraction having a density of 0.920-0.940 g/cm<SUP>3</SUP>, and the weight ratio of the LMW fraction to the HMW fraction being from 30:70 to 55:45. |