摘要 |
A high-strength and high-toughness martensitic stainless steel, which is excellent in corrosion resistance to carbon dioxide, and which has no risk of cracking, even if used as welded under cathodic protection. The steel has the following basic composition (1) and satisfies the following condition (2). (1) The composition containing, on a mass basis, C: not greater than 0.04%, Cr: 7-15%, Ni: 0.7-8.0%, Al: 0.001-0.20%, or further containing one or more of Si, Mn, Cu, S, Nb, Ti, Zr, Mo, W, Ca, Mg, and La in a specified amount. (2) The following inequalities (1) and (2) are satisfied. M=98+47C-1.1Cr+1.4Ni-150Al-200Nb-50Ti-200Zr-22(Mo+0.5W)>/=50 P</=0.046-0.0008HRC where the symbols of the elements in the inequalities (1)-1 to (1)-4 and (2) indicate the contents (% by mass) of the respective elements, and HRC in the inequality (2) indicates the Rockwell C-scale hardness of the steel as quenched. <IMAGE> |
申请人 |
SUMITOMO METAL INDUSTRIES LIMITED |
发明人 |
UEDA, MASAKATSU;TAKABE, HIDEKI;KONDO, KUNIO;OGAWA, KAZUHIRO;AMAYA, HISASHI |