| 摘要 |
A TRIP-type high strength steel plate having good workability is provided which, while reducing the amount of alloying elements added which increase the production cost, ensures a contemplated retained austenite structure, has good adhesion to zinc plating, and can also be applied to highly corrosion resistant surface treated steel plates. The high strength steel plate having improved workability and plating adhesion is such that a high concentration, i.e., 0.03 to 2.0% by weight, of nitrogen is incorporated, the contents of silicon and aluminum, which form nitride, are preferably regulated respectively to not more than 0.5% by weight and not more than 0.3% by weight, and, in addition, calcium, sodium, magnesium, etc. are optionally added to control the formation of iron nitride, whereby the volume fraction of the retained austenite phase in the metal structure is regulated to 3 to 20% by weight. |