CHARGING MATERIAL FOR PRODUCING REFRACTORY HIGH-STRENGTH SPHERICAL GRANULES AND METHOD FOR THE PRODUCTION THEREOF

摘要

The inventive method for producing refractory high-strength spherical granules consists in separately presintering kaolin and bauxite in a rotational furnace, jointly sintering said components in order to produce a charging material, granulating, drying and screening said charging material, sintering said granules in the rotational furnace and screening the sintered granules. Said sintered kaoline is produced by sintering at a temperature ranging from 1400 to 1500 DEG C so far as a water absorption of 5% is attained for kaoline containing 40-45 mass% and a free quartz in a quantity equal to or greater than 60 mass%. The Al2O3: SiO2 ratio in the charging material is equal to 1:1 at the following charging material component ratio: 36-67 mass% sintered kaolin and the rest being sintered bauxite.