| 摘要 |
FIELD: refractory industry, in particular corundum parts for ferrous and non-ferrous metallurgy. ^ SUBSTANCE: on the step of batch preparation surface of fused corundum filler spheroid particles is damped with oleic or stearic acid in amount of 0.5-0.0 mass % in respect to total mass of phosphate binder. During agitation fine dispersed intergrinding mixture containing (mass %): Al2O3 47-80, ZrO2-SiO2 20-53, and phosphate binder (e.g. phosphoric acid or aluminum phosphate) is added. Batch contains (mass %): fused corundum filler 50-70; fine dispersed intergrinding mixture 30-50; phosphate binder over 100 % 5-10. Batch is homogenized, formed, solidified in air, baked at decomposition temperature of zircon concentrate, and cooled with isothermal holding at 1100-9000C. ^ EFFECT: corundum-based articles with improved strength and heat resistance. ^ 7 cl, 2 tbl |