<p>PURPOSE:To improve the abrasion resistance, the printing characteristic and the visibility of the transparent conductive film by forming the conductive film on one surface of a film base, and sticking the specific transparent base on the other surface. CONSTITUTION:The transparent conductive film 2 having the thickness more than 50Angstrom and made of the compound oxide compounded of the indium oxide and the tin oxide is formed on one surface of the base 1 made of the transpar ent PET film having 2-120mum of the thickness. Next, the acrylic and transparent adhesive layer 3 having 1X10<5>-1X10<7>dyn/cm<2> of the elastic coefficient and the thickness more than 1mum is formed on the other surface of the base 1 so as to form the conduction processed film. The toluene solution is coated on one surface of the transparent base 4 having 75mum of the thickness so as to form the hard coat processed layer 5, and the opposite surface of the layer 5 is stuck to the conduction processed film through the adhesive layer 3. The laminated film is thus obtained.</p> |