A process for making an alkaline resistant material comprises the steps of grinding together 0-40% light magnesia, 0-80% roasted magnesia, 10-54% ceramic clay, 0-9% limestone, 1-4% water glass, 0-1.5% carboxymethyl cellusolve, 0-27% talc, 0-3% calcium or barium carbonate to a particle size of less than 50 microns, mixing the ground mixture with water to produce a paste containing <23% wt. water, shaping the paste to a desired shape, drying the shaped product at a temperature of 110 degrees Centigrade, and firing the dried shaped product in a kiln at 1350 degrees Centigrade. The resulting alkali resistant ceramic contains 25-76 wt % MgO, 13-47% SiO2, 5-20 wt % Al2O3, and 1-10 wt % Fe2O3, CaO, K2O, and/or Na2O, with forsterite and spinel being the dominant crystalline phases.
|