The invention relates to a method for producing a siderurgical product made of carbon steel having a high copper content, according to which:-a liquid steel having the composition: 0.0005% 1%; 0.5 Cu 10%; 0 Mn 2%; 0 Si 5% 0 Ti 0.5%; 0 Nb 0.5%; 0 Ni 5%; 0 Al 2%, the remainder being iron and impurities, is produced;-said liquid steel is poured directly in the form of a thin strip having a thickness of no more than 10 mm;-the strip is subjected to forced cooling and/or is surrounded by a non-oxidizing atmosphere while having a temperature of more than 1000? C;-said thin strip is hot rolled at a reduction rate of at least 10%, the temperature at the end of the rolling process being such that all of the copper is still in a solid solution in the ferrite and/or austenite matrix;-and the strip is coiled. The invention also relates to a siderurgical product obtained according to said method.
|