| 摘要 |
This invention is a method of manufacturing oxide porous bodies and components of alumina and magnesia, using alumina and magnesia powders as raw materials, wherein (1) cold isostatic pressure (CIP) of at least 100 MPa is applied to the materials to introduce a plastic deformation with lattice disorder in the surface vicinity without external changes in the particles, (2) by sintering (calcining) the powders with the above described plastic deformation, the microscopic plastic deformation is removed and, at the same time, formation and growth of necks between grains is induced, (3) from the above described steps (1) and (2), a highly porous body with a structure constituted by a three dimensional network of grains connected through the necks is produced.
|