| 摘要 |
A work-hardened poppet exhaust valve for internal combustion engines is obtained from a solutioned work-hardenable austenitic stainless steel coil or bar stock in which chromium is present in the range of 13%-25% by weight, nickel is present in the range of 4%-16% by weight, manganese is present in the range of 0.25%-8% by weight, copper is present in the range of 0.5%-7% by weight, the interstitial elements carbon plus nitrogen are present in a total amount less than 0.45% by nitrogen are present in a total amount less than 0.45% by weight, and at least one refractory metal selected from the group consisting of molybdenum, niobium, vanadium, tungsten and tantalum is present in the range of 1%-5% by weight. The coil or bar stock is extruded to a poppet valve preform configuration at a temperature in the range of room temperature to 1,000° F., and at a true strain of more than 0.8. The parameters of extrusion provide said work-hardened poppet valve with a stem hardness more than Rc=25.
|