On a substrate at a temperature of 120 to 240° C., Fe and Pt monatomic layers are alternately laminated. The magnetic multilayer film obtained by such a method has an L10 ordered structure so as to exhibit a high magnetic anisotropy energy constant, a (001) surface parallel to the substrate surface, and a high perpendicular magnetic anisotropy, while its coercive force in a direction perpendicular to the substrate surface and the squareness ratio of its magnetization curve in a direction perpendicular to the substrate surface are large, so that it is usable as a magnetic recording film for a magnetic recording medium and the like. Also, since the magnetic multilayer film is formed while the substrate temperature is 120 to 240° C., the temperature load on the substrate or the like is lowered as compared with conventional making methods in which the substrate temperature is about 500° C.
|