| 摘要 |
A low-temperature firing ceramic composition contains Sr2MgSi2O7 crystals forming a major crystal phase of the composition. This composition can be produced, for example, by a process including the steps of (a) mixing together a silica powder, a magnesia powder and a strontium oxide powder to obtain a powder mixture; (b) subjecting the powder mixture to a calcination at a temperature of 1,000-1,200° C. to obtain a calcination product containing Sr2MgSi2O7 crystals; (c) mixing the calcination product with alumina powder, boron oxide powder, lithium oxide powder, binder and ethanol to obtain a powder mixture; (d) granulating the powder mixture; (e) shaping the resulting granules into a green body; (f) compacting the green body by a hydrostatic pressing (CIP); and (g) firing the resulting compact in an atmosphere of air, thereby obtaining the composition. A wiring substrate includes a laminate of green sheets, each containing Sr2MgSi2O7 crystals, and a wiring pattern formed in an inside of the laminate and/or on a surface of the laminate.
|