| 摘要 |
The present invention relates to a wire rod for high fatigue-strength steel wire of small diameter, and a wire rod used in steel wire obtained by twisting these together, a steel wire and a method of producing the same. The wire rod for steel wire and the steel wire have a microstructure obtained by controlled cooling following hot rolling of a steel, containing, in mass %, 0.6-1.3% of C, 0.1-1.5% of Si and 0.2-1.5% of Mn wherein the area ratio of upper bainite measured in a cross-section thereof is 5-50%, the remainder being substantially composed of pearlite. The production method thereof comprises drawing and patenting a wire rod of 5-16 mm diameter having the aforesaid composition to obtain a wire of 0.8-2.8 mm diameter, then austenitizing the wire, quenching it to a temperature range of 500-560° C. for conducting isothermal transformation, thereby adjusting it to a steel microstructure wherein the area fraction of upper bainite is 5-50%, the remainder being substantially composed of pearlite, and then conducting brass plating and drawing to obtain a wire of 0.05-1.0 mm diameter.
|