OXYGEN BARRIER COATING AND COATED FILM

摘要

A film with excellent oxygen barrier properties is disclosed. A barrier coating used thereon is also disclosed, including polyvinyl alcohol and a copolymer of maleic acid and acrylic acid, and wherein the copolymer of maleic acid and acrylic acid has a weight average molecular weight of about 3500 to about 5000. The barrier coating is typically less than about 1 micrometer in thickness and provides an oxygen barrier of less than about 0.3 cc.mil/100 in2/day/atm when tested at 23 degrees Celsius and 0 percent relative humidity according to ASTM D3985. A method of stripping low molecular weight fractions from the copolymer is also disclosed. Metallized coated film according to the present invention shows surprising barrier properties.