摘要 |
PURPOSE: A method for fabricating mold flux granule for continuous casting by spray drier is provided to improve heat insulation property of molten steel and fusibility of mold flux by drying the mold flux granule after spraying granular mold flux granule a grain size of which is minimized onto the upper surface of molten steel in a mold. CONSTITUTION: The method for fabrication mold flux granule for continuous casting by spray drier comprises the processes of charging aqueous slurry containing flux constituents including carbon particulate into a dryer; and drying the granules after spraying uniformed granules having a constant size formed from the charged aqueous slurry by raw material spraying process using the centrifugal force onto the upper surface of molten steel, wherein the uniformed spherical granules are sprayed and dried by applying a centrifugal disc to the dryer in the aqueous slurry spraying process, and the spherical granules manufactured by the aqueous slurry spraying process have a diameter of 0.032 to 0.25 mm.
|