| 摘要 |
The present invention provides: a fabrication method of a silicon carbide sintered body, including a step of fabricating a mixed powder slurry by dissolving or dispersing silicon carbide powder, at least one organic material composed of a nitrogen source, and at least one organic material composed of a carbon source or carbon powder in a solvent, a step of fabricating a green body by pouring the mixed powder slurry into a mold and drying and a step of filling pores in the green body by immersing the green body in high purity metallic silicon that has been heated to 1450 to 1700 DEG C in a vacuum atmosphere or inert gas atmosphere and melted, and generating silicon carbide by reacting silicon sucked up into the pores in the green body by capillary action with free carbon in the green body; and a silicon carbide sintered body obtained by a reaction sintering method, having a density of 2.90 g/cm<3> or more and a volume resistivity of 10<0> OMEGA . cm or less, and containing nitrogen at 150 ppm or more. <IMAGE> |