| 摘要 |
An oil-extended rubber comprising 100 weight parts of a rubber ingredient comprising a conjugated diene rubber wherein the ratio (Mw/Mn) of weight average molecular weight (Mw) to number average molecular weight (Mn) is in the range of 1.2 to 2.2, and the conjugated diene monomer units have a vinyl bond unit content of at least 20%, and 5-100 weight parts of a process oil having a total acid value of not larger than 1.0 mgKOH/g, a pour point of not higher than 50 DEG C and an aromatic carbon content of at least 20%. A rubber composition comprising 100 weight parts of the above-mentioned rubber ingredients, 5-100 weight parts of the process oil and 10-200 weight parts of a reinforcing agent. This rubber composition gives a crosslinked article having high tensile strength, high abrasion resistance and reduced heat build-up, and is useful, for example, as an automobile tire material. |