A high-strength, high-toughness martensitic stainless steel sheet has a chemical composition comprising, in mass percent, more than 0.03 to 0.15% of C, 0.2-2.0% of Si, not more than 1.0% of Mn, not more than 0.06% of P, not more than 0.006% of S, 2.0-5.0% of Ni, 14.0-17.0% of Cr, more than 0.03 to 0.10% of N, 0.0010-0.0070% of B, and the balance of Fe and unavoidable impurities and has an A value of not less than -1.8, where A value=30(C+N)-1.5Si+0.5Mn+Ni-1.3Cr+11.8. The suitability of the steel sheet as a gasket material is enhanced by producing it to include not less than 85 vol % of martensite phase and to have a spring bending elastic limit Kb0.1 after application of tensile strain of 0.1% of not less than 700 N/mm2. Edge cracking during cold rolling is inhibited by conducting cold rolling after subjecting the hot-rolled sheet to 600-800 ° C.x10 hr or less intermediate annealing to impart a steel hardness of not greater than Hv 380.
|