摘要 |
A sintered ceramic for a scintillator having a composition represented by the general formula of Gd3-xCexAlySizGa5-y-zO12, wherein 0.001<=x<=0.05, 1<=y<=4, and 0.0015<=z<=0.03, is produced by mixing gadolinium oxide, aluminum oxide, gallium oxide, a cerium salt, a silicon compound and a fluorine compound in such proportions as to provide the above composition; calcining the resultant mixture at a temperature of 1400-1600° C.; disintegrating the resultant calcined body to ceramic powder; pressing the ceramic powder to provide a green body; and sintering the green body at a temperature of 1600-1700° C. in a non-oxidizing atmosphere at 5x104 Pa or more, and optionally further by hot isostatic pressing at a temperature of 1400-1600° C. in an argon atmosphere.
|