An alloy has a composition of, in weight percent, from about 16 percent to about 21 percent chromium, from about 6 percent to about 12 percent iron, from about 6 percent to about 12 percent cobalt, from about 2.8 percent to about 3.3 percent molybdenum, from about 5 percent to about 5.4 percent niobium, from about 0.2 percent to about 2 percent tantalum, from about 0.65 percent to about 1.15 percent titanium, from about 0.2 percent to about 0.8 percent aluminum, from about 0.01 percent to about 0.05 percent carbon, from about 0.005 percent to about 0.01 percent boron, less than about 0.1 percent zirconium, balance nickel and impurities. A billet of this alloy is heated to an initial forging temperature of from about 1800 DEG F to about 2100 DEG F, and forged beginning at the initial forging temperature. The alloy may also be readily welded. <IMAGE> |