| 摘要 |
<p>The process for forming a microporous polymeric semi-crystalline film, involving the steps of cold compressive extruding a precursor film, preferably in a biaxial fashion, so as to compress the film by a factor of about 2 to 1 to about 10 to 1, stretching the film by about 100 to about 500 percent, preferably in a biaxial fashion, and heat annealing either before, during, or preferably after the stretching step at a temperature up to the alpha transition temperature of the polymer for a time sufficient to maintain the microporous character of the final film.</p> |