POLYOXYMETHYLENE RESIN COMPOSITION AND MOLDING PRODUCT INCLUDING THE SAME

摘要

The present invention relates to a polyoxymethylene resin composition and a molded product formed of the resin composition. The polyoxymethylene resin composition comprises: a base resin including polyoxymethylene, which has the weight reduction less than or equal to 0.25% after heating the same for 10 to 30 minutes at the temperature in the range of 200-220°C; 1.0 to 3.0 parts by weight of aluminum flake, with respect to 100 parts by weight of the base resin; 0.1 to 0.5 parts by weight of polyhydric alcohol fatty acid ester; 0.1 to 0.5 parts by weight of an acrylate-styrene copolymer; and 0.05 to 0.5 parts by weight of a dihydrazide compound. Provided in the present invention is the polyoxymethylene resin composition, which can maintain material properties such as excellent mechanical strength and shock resistance.