| 摘要 |
A method for electrochemical phosphating of metal surfaces, particularly stainless steel, in connection with cold forming of metal workpieces, which method provides the cold formed workpiece with a lubricant after phosphating, involves an electrochemical phosphating through a cathodic process applying an aqueous phosphating solution containing0.5 to 100 g Ca2+/l0.5 to 100 g Zn2+/l5 to 100 g PO43-/l0 to 100 g NO3-/l0 to 100 g ClO3-/l and0 to 50 g F- or Cl-/lby which the temperature of the solution is between 0 and 95° C., the pH-value of the solution is between 0.5 and 5, and the current density is between 0.1 and 250 mA/cm2. This gives a good lubrication effect, a good adhesion to the metal surface, particularly stainless steel, and a more expedient texture than ordinary phosphating. |