| 摘要 |
The present invention relates to galvanized steel having a high aluminum content in the coating, as well as a batch hot-dip galvanization process for making such steel. The galvanized steel herein has a coating comprising an inner layer of intermetallic iron aluminum compounds, such as Fe2Al5 (which may have some zinc present), and an outer layer of intermetallic zinc aluminum compounds containing from about 17% to about 40% (preferably about 22%, the Zn-Al eutectoid) aluminum (which may have some iron present). The batch hot-dip galvanization process for making such steel comprises: (a) fluxing the steel by electroless plating on the surface of the steel of a metal such as tin, copper or nickel; and (b) dipping the fluxed steel into a molten galvanization bath comprising zinc and from about 17% to about 40% aluminum.
|