The invention aims to provide a manganese-zinc ferrite exhibiting a high initial permeability over a broad band and especially in a low-frequency region of about 10 kHz and a method for preparing the same. A method for preparing a manganese-zinc ferrite by firing is characterized in that the firing includes a main temperature holding step at 1,200-1,450° C. and a thermal ramp-down step prior to the main temperature holding step, and the lowest temperature reached by the mid-firing thermal ramp-down step is set in the range of 1,000-1,400° C. and lower by at least 50° C. than the hold temperature of the main holding step, thereby obtaining a manganese-zinc ferrite comprising 50-56 mol % calculated as Fe2O3 of iron oxide, 22-39 mol % calculated as MnO of manganese oxide, and 8-25 mol % calculated as ZnO of zinc oxide as main components, and having a mean crystal grain size of more than 50 mum to 150 mum.
|