<p>A thermally conductive heat-resistant silicone rubber composite sheet which has a heat-resistant resin film layer on at least one side of a silicone rubber sheet and can be suitably used in a hot pressing process, with the silicone rubber sheet being a sheet molded of a silicone rubber composition that comprises (A) 100 parts by weight of organopolysiloxanes having an average polymerization degree of at least 200, (B) 0 to 150 parts by weight of carbon black containing volatile impurities except water in a content of at most 0.5 weight %, (C) 0 to 1,600 parts by weight of at least one thermally conductive substance selected from the group consisting of metals, metal oxides, metal nitrides and metal carbides and (D) a curing agent, provided that the total proportion of the components (B) and (C) is from 10 to 1,600 parts by weight, and having a volatile impurity content of at most 0.2 weight % when it is heated at 150 DEG C for 3 hours: and a method of producing the aforesaid composite sheet.</p> |