PROBLEM TO BE SOLVED: To obtain a resin composition improved in dispersibility, etc., of inorganic filler in long-term molding by including an ethylene-vinyl acetate copolymer saponified product, inorganic filler and a specific metallic soap. SOLUTION: This resin composition comprises (A) 100 pts.wt. ethylene-vinyl acetate copolymer saponified product having preferably 1-100 g/10 min melt index (at 210 deg.C under 2160 g load), 20-60 mol% ethylene content and >=90 mol% saponification degree, (B) 1-100 pts.wt. inorganic filler (e.g. silicon oxide) having preferably 0.1-10μm particle diameter and (C) 0.005-1 pt.wt. metallic soap of the formulaαMO.M(OOCR)2 [αis 0.1-1.0; M is a divalent metal of the group II of the periodic table; R is an 11-29C (un)saturated alkyl] obtained by reacting (i) a 12-30C aliphatic monocarboxylic acid with (ii) a (hydr)oxide of the group II metal of the periodic table under heating by a dry type direct method.
|