Nickel base superalloy preweld heat treatment

摘要

A preweld heat treatment for precipitation hardenable IN939 nickel base superalloy having a gamma matrix and gamma prime strengthening phase dispersed in the matrix comprises heating the nickel base superalloy at about 2120 degrees F. for a time to solution gamma prime phase followed by slow cooling to below about 1450 degrees F. at a rate of about 1 degree F./minute or less, and cooling to room temperature. The preweld heat treatment eliminates strain age cracking at base metal weld heat-affected zone upon subsequent heat treatment to develop alloy mechanical properties.