Refining elements for refining discs for disc refiners for the manufacture of mechanical pulp, for example, board pulp, are subjected to hard abrasive wear in acid environment and at high temperature. In order to improve the wear resistance alloys with precipitated carbides are used. A service life improved in comparison with known alloys is obtained with a refining disc with the following analysis in % by weight: 2.96 C, 0.77 Si, 0.82 Mn, 24.2 Cr, 5.16 V, 0.04 Ni, 0.03 Mo, and the remainder Fe and impurities. After casting, the refining segments are hardened and annealed and assume a hardness of 57-63 HRC. |