发明名称 |
METHOD FOR MANUFACTURING VANADIUM CARBIDE POWDER ADDED TOOL STEEL BY MILLING PROCESS |
摘要 |
Vanadium carbide powder mixed with 5-15wt% tool steel power is given by ball milling for 120 hours in hexan, wet atmosphere, annealed for 1 hour at the temperature 900 degree C in the vacuum state less than 100 tor, having a 0.5-1wt% lubricant added therein, cool molded, and in partial reducing atmosphere, heated at the temperature 500-600 degree C so as to remove the lubricant. Also, it is sintered at the proper temperature of 1220-1300 degree C in the vacuum state less than 100 tor.
|
申请公布号 |
KR970005415(B1) |
申请公布日期 |
1997.04.16 |
申请号 |
KR19940015938 |
申请日期 |
1994.07.04 |
申请人 |
KOREA INSTITUTE OF MACHINERY & METALS |
发明人 |
JUNG, HYUNG-SIK;BAE, JONG-SOO;KIM, YONG-JIN |
分类号 |
C22C33/02;(IPC1-7):B22F9/00;B22F1/00;B22F3/12 |
主分类号 |
C22C33/02 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|