| 摘要 |
PVP-coated asymmetric hollow fibers made from SIXEFT TM -Durene, a polyimide made from 2,2-bis[3,4-dicarboxyphenyl] hexafluoropropane dianhydride and 2,3,5,6-tetramethylphenylene diamine monomers, and a process for making such fibers. These coated fibers have a separation factor that exceeds 6 for oxygen and nitrogen and a permeance of at least about 10 ppm cc(STP)/(sec cm2 cm-Hg). A polymer dope comprising SIXEF TM -Durene in a solvent system containing N-methyl-2-pyrrolidone ("NMP") and an organic acid such as propionic acid ("PA") is prepared by polymerizing the polyimide monomers in NMP to form a polyamic acid polymer and imidizing this polymer using the acid anhydride. Water released from the polymer in the imidization reaction converts the anhydride to acid. The dope is wet-spun into hollow fibers; the fibers are coagulated in water. The fibers are then evenly coated with PVP, preferably by dipping the fibers in a dilute PVP solution. |